N i t r i d e s
| state | material | data | range (micron) | Temperature | reference (and link) |
|---|---|---|---|---|---|
| cry. | α-Si3N4 (thin film) | absorbance & mass absorption coefficent k[cm2g-1][fig] [fig.] |
2.5-200 2.5-25mm (4000-400cm-1) 200-15mm (50-650cm-1) |
Pitman et al. (2006) MNRAS | |
| cry. | β-Si3N4 (thin film) | absorbance & mass absorption coefficent k[cm2g-1][fig] [fig.] |
2.5-200 2.5-25mm (4000-400cm-1) 200-15mm (50-650cm-1) |
Pitman et al. (2006) MNRAS | |
| cry. (nanocrystalline) | AlN (Aluminum nitride) (thin film) | absorbance & mass absorption coefficent k[cm2g-1][fig] [fig.] |
2.5-200 2.5-25mm (4000-400cm-1) 200-15mm (50-650cm-1) |
Pitman et al. (2006) MNRAS | |
| cry. | Mg3N2 (Magnesium nitride)(thin film) | absorbance & mass absorption coefficent k[cm2g-1][fig] [fig.] |
2.5-200 2.5-25mm (4000-400cm-1) 200-15mm (50-650cm-1) |
Pitman et al. (2006) MNRAS | |
| cry. | Ca3N2 (Calcium nitride) (thin film) | absorbance & mass absorption coefficent k[cm2g-1][fig] [fig.] |
2.5-200 2.5-25mm (4000-400cm-1) 200-15mm (50-650cm-1) |
Pitman et al. (2006) MNRAS | |
| amor. | Fe-C nanocomposites | Transmision [fig.] | 0.3 -50 μm (VIS-IR) | 20-300K | Jäger C. et al. (2006) Ap. plied Physics A, Vol85, Issue 1, pp.53-62 |
state: amor. - amorphous, cryst. - crystalline, glas. - glassy.
data: m.abs.c. - mass absorption coefficient, cond. - conductivity, n,k - refractive index; (T) - dependence on temperature; [fig] - figure, [tab] - table, (c!) - compilation.